Hot Dipped Galvanized Steel Wires for Binding Wire Uses

Hot-dipped galvanized steel wires are a popular choice for binding applications due to their excellent corrosion resistance and durability. The zinc coating, applied through a hot-dip process, protects against rust and other forms of corrosion, making them ideal for harsh environments. Available in diameters from 0.5mm to 5.0mm (0.02" to 0.2"), these versatile wires are used in construction, agriculture, packaging, and other industries. Their strength, flexibility, and corrosion resistance make them a reliable choice for securing materials.

Material

• The Hot Dipped Galvanized Steel Wires are manufactured using high-quality low carbon steel, which provides the necessary strength and flexibility for various binding applications. The wires are processed through drawing, annealing, and hot-dip galvanizing, ensuring a durable zinc coating that enhances corrosion resistance.

Type

• These wires are categorized as Hot Dipped Galvanized Binding Wires, specifically designed for applications requiring superior rust resistance and durability. They are suitable for use in construction, agriculture, and packaging industries where binding strength and longevity are critical.

Wire Diameter (GA)

Hot Dipped Galvanized Steel Binding Wires are available in a range of diameters to suit different binding needs.

• 0.90 mm (20 GA), with a zinc coating of at least 130 g/m²
• 1.25 mm (18 GA), with a zinc coating of at least 170 g/m²
• 1.60 mm (16 GA), with a zinc coating of at least 195 g/m²
• 2.00 mm (14 GA), with a zinc coating of at least 210 g/m²
• 2.50 mm (12 GA), with a zinc coating of at least 215 g/m²
• 3.05 mm (10 GA), with a zinc coating of at least 225 g/m²

Standard Shapes

• The wires are typically wound into big coils, which are convenient for handling and transportation. These coils maintain the integrity of the wire, preventing unwinding or tangling, making them efficient for industrial use.

Rolls Size

• The coils are produced in large sizes with an inner diameter ranging from 340 mm to 500 mm (13.4 inch to 19.7 inch) and an outer diameter between 850 mm to 900 mm (33.5 inch to 35.4 inch). Each coil weighs approximately 550 to 650 kilograms (1212 to 1433 pounds), ensuring a substantial supply of wire for extensive binding operations.

Standards

• These Hot Dipped Galvanized Steel Binding Wires meet stringent technical requirements, including a tensile strength of 340 - 500 N/mm², ensuring they can withstand significant stress. The wires also pass a wrapping test around a mandrel, ensuring flexibility and durability without breaking. The elongation at break is maintained at 10% for all sizes, with the exception of 0.90 mm wire, which has a minimum elongation at break of 7.5%.

Color

• The wires have a bright, silver-colored finish, typical of hot-dip galvanized products, which also visually indicates the presence of the protective zinc coating.

Customization

• Customization options are available for wire diameter, zinc coating thickness, and coil size to meet specific customer requirements. This ensures that the wire can be tailored for specialized binding applications in various industries.

Packaging

• The wires are packed in large coils, secured to prevent unwinding during transport. Each coil is carefully wrapped to protect the wire from external damage and ensure easy handling during installation. The robust packaging ensures that the wire maintains its integrity and quality from manufacturing to end-use.

HDG Binding Wire 0.90 mm, zinc coating min. 130 g/m2
HDG Binding Wire 1.25 mm, zinc coating min. 170 g/m2
HDG Binding Wire 1.60 mm, zinc coating min. 195 g/m2
HDG Binding Wire 2.00 mm, zinc coating min. 210 g/m2
HDG Binding Wire 2.50 mm, zinc coating min. 215 g/m2
HDG Binding Wire 3.05 mm, zinc coating min. 225 g/m2